Plastic Bright Lubricant: KS-101a (aka HEEBS)
Product introduction
This product is based on the introduction of polar groups on the basis of ethylene bis fatty acid amide. Due to the introduction of this group, its performance has better dispersibility in addition to EBS characteristics. Bright lubricity is a highly efficient plastic lubricant and pigment. Dispersant. This product is white or yellowish powder and granules (fine powder grade is 95 mesh 95%). It is insoluble in water, ethanol, acetone, carbon tetrachloride and other solvents at room temperature, but soluble in hot halogenated hydrocarbons. Acid, alkali, non-toxic.
Technical data
Melting point: ≥ 65 (°C) Color ≤ 5.0 (Gardner)
Heating loss ≤ 0.5% (WT) Flash point ≥ 275 °C
Acid value ≤ 10.0 kohmg / g amine value ≤ 10.0 kohmg / g
Thermal weight loss (%WT) 250°C ≤1.8; 300°C ≤ 4.8
main application
It is added in the amount of 3 to 5% in PE, PP, PVC and polypropylene masterbatch, and 5 to 8% in aBS masterbatch. It has good dispersibility for pigments (especially carbon black) and can improve MFR of the masterbatch and surface brightness.
main application
Adding 0.5PHR to polypropylene granulation reduces screw torque by 40%, which increases production, saves energy and reduces machine wear.
main application
As a dispersing agent for the nano Ti02 masterbatch in the nano-T0O 2 /HIPS composite, it is added in an amount of 3 to 5%.
main application
Inorganic filled modified PP as a brightener and phase solvent can improve the brightness, melt index, notched impact strength, flexural modulus and breaking strength of the product. The amount added is 0.5 to 1.5 PHR.
main application
The recovery of aBS, PS, and aS is enhanced by light lubrication, and the amount of addition is 1.0 to 1.2 PHR.
main application
When pigment color matching, the amount of KS-101a (fine powder grade) can be expressed by a simple formula:
Pigment specific surface area * 100% (wt%)
___________ 5
Reference dosage:
Inorganic Pigment / Titanium Dioxide: 0.5 to 1.0% (wt%)
Organic pigment: 5 to 12% (wt%)
Ordinary carbon black: 8 to 20% (wt%)
High pigment carbon black: 40 to 60% (wt%)
KS-101a is particularly effective for the particularly difficult-to-disperse pigments of indigo, indigo, and carbon black.
main application
It can be used as a brightener in PE packaging film.
main application
Adding 0.3~0.5PHR to transparent PVC, PP and PE can produce good lubrication and anti-sticking effect (PVC is plasticized and not plasticized).
main application
Adding 0.5PHR to hard PVC profiles and plates can replace stearic acid for external lubrication and not easy to bloom.
Food law situation
KS-101a (HEEBS) complies with multi-country food regulations and can be used in food contact applications such as Bgvv and FDA.
Packaging and transportation
Kraft paper composite woven bag 20 kg / bag.
This product should be protected from direct sunlight and rain during transportation. The storage area should be ventilated. The product is stored and transported as normal chemicals.